Characterization of Ti-6Al-4V alloy foams synthesized by space holder technique
(Elsevier Science Sa, 2011) Esen, Ziya; Esen, Ziya; Bor, Sakir; 52373; Ortak Dersler Bölümü
Ti-6Al-4V foams, biomedical candidate materials, were synthesized by powder metallurgical space holder technique as a result of evaporation of magnesium to achieve desired porosity content. Final products contained porosities in the range similar to 43-64% with an average macropore size between 485 and 572 mu m and a lamellar type Widmanstatten microstructure composed of alpha-platelets and beta-laths. Unlike the case of bulk Ti-6Al-4V alloy tested under compression loading, compression stress-strain curves of manufactured Ti-6Al-4V foams were similar to those of elastic-plastic foams, which contain a linear elastic region; a plateau stage: and a densification stage. In the plateau region deformation bands perpendicular to the compression axis were developed and cell collapsing took place together with the buckling and fracture of some of the cell walls and edges in a ductile manner. Calculated elastic modulus and yield strength were in the range 1.42-14.7 GPa and 28.2-150 MPa, respectively, and the foam mechanical properties were found to be dependent on micro porous cell wall properties, which in turn depends on neck size between powder particles. Around 330 MPa yield strength value was calculated for porous cell walls by the use of Ti-6Al-4V alloy powder samples sintered in loose and compacted conditions, which were utilized to simulate the cell wall structure of foams. In addition, overall mechanical properties of foam s were investigated considering macro porosity fraction, p(macro), and the yield strength of foams exhibited a power law dependence, similar to commonly used minimum solid area models, in the form of A*(1 - p(marco))(n), where the proportionality constant "A" was found to be the yield strength of micro porous cell walls. (C) 2011 Elsevier B.V. All rights reserved.
Citation - WoS: 14
Citation - Scopus: 16
Characterization of Ti6Al7Nb alloy foams surface treated in aqueous NaOH and CaCl2 solutions
(Elsevier Science Bv, 2016) Butev, Ezgi; Esen, Ziya; Esen, Ziya; Bor, Sakir; 47423; 52373; Ortak Dersler Bölümü
Ti6Al7Nb alloy foams having 53-73% porosity were manufactured via evaporation of magnesium space holders. A bioactive 1 mu m thick sodium hydrogel titanate layer, NaxH2-xTiyO2y+1., formed after 5 M NaOH treatment, was converted to crystalline sodium titanate, Na2TiyO2y+1, as a result of post-heat treatment. On the other hand, subsequent CaCl2 treatment of NaOH treated specimens induced calcium titanate formation. However, heat treatment of NaOH-CaCl2 treated specimens led to the loss of calcium and disappearance of the titanate phase. All of the aforementioned surface treatments reduced yield strengths due to the oxidation of the cell walls of the foams, while elastic moduli remained mostly unchanged. Accordingly, equiaxed dimples seen on the fracture surfaces of as-manufactured foams turned into relatively flat and featureless fracture surfaces after surface treatments. On the other hand, Ca- and Na-rich coating preserved their mechanical stabilities and did not spall during fracture. The relation between mechanical properties of foams and macro-porosity fraction were found to obey a power law. The foams with 63 and 73% porosity met the desired biocompatibility requirements with fully open pore structures and elastic moduli similar to that of bone. In vitro tests conducted in simulated body fluid (SBF) showed that NaOH-heat treated surfaces exhibit the highest bioactivity and allow the formation of Ca-P rich phases having Ca/P ratio of 1.3 to form within 5 days. Although Ca-P rich phases formed only after 15 days on NaOH-CaCl2 treated specimens, the Ca/P ratio was closer to that of apatite found in bone. (C) 2016 Elsevier Ltd. All rights reserved.
Citation - WoS: 22
Citation - Scopus: 25
In Vitro Bioactivity Investigation of Alkali Treated Ti6al7nb Alloy Foams
(Elsevier, 2015) Butev, Ezgi; Esen, Ziya; Esen, Ziya; Bor, Sakir; 47423; Ortak Dersler Bölümü
Biocompatible Ti6Al7Nb alloy foams with 70% porosity manufactured by space holder method were activated via alkali treatment using 5 M NaOH solution at 60 degrees C. The interconnected pore structures enabled formation of homogenous sodium rich coating on the foam surfaces by allowing penetration of alkali solution throughout the pores which had average size of 200 mu m. The resulted coating layer having 500 nm thickness exhibited porous network morphology with 100 nm pore size. On the other hand, heat treatment conducted subsequent to alkali treatment at 600 degrees C in air transformed sodium rich coating into crystalline bioactive sodium titanate phases. Although the coatings obtained by additional heat treatment were mechanically stable and preserved their morphology, oxidation of the samples deteriorated the compressive strength significantly without affecting the elastic modulus. However, heat treated samples revealed better hydroxyapatite formation when soaked in simulated body fluid (SBF) compared to alkali treated foams. On the other hand, untreated surfaces containing bioactive TiO2 layer were observed to comprise of Ca and P rich precipitates only rather than hydroxyapatite within 15 days. The apatite formed on the treated porous surfaces was observed to have flower-like structure with Ca/P ratio around 1.5 close to that of natural bone. (C) 2014 Elsevier B.V. All rights reserved.