Characteristic Features of Thermoluminescence in Neodymium-Doped Gallium Sulfide
(Wiley, 2018) Isik, M.; Ahmedova, F.; Guseinov, A.; Gasanly, N.; Guler, I.; 101531
The thermoluminescence (TL) of neodymium-doped gallium sulfide (GaS:Nd) single crystals was measured from 10 K to room temperature with various heating rates between 0.2 and 1.0 K/sec. Two peaks centered at 70.9 K and 116.0 K were observed when using a heating rate of 0.8 K/sec. Initial rise and curve fitting methods were used to obtain information on trap activation energies. Activation energies of 94 and 216 meV were found for two analyzable peaks. The heating rate dependencies of TL intensities revealed that one of the observed peaks showed normal behavior according to the one trap-one recombination model, whereas the other model showed anomalous heating rate behavior. TL experiments were also carried out at different illumination temperatures from 10 to 32 K; maximum peak temperature remained almost the same at various illumination temperatures. This behavior indicated that the revealed trapping centers are single, discrete levels. The TL glow curves of undoped GaS crystals were also investigated and the effect of Nd doping on the TL characteristics of crystals is discussed in the manuscript.
Citation - WoS: 5
Citation - Scopus: 5
Determination of Trapping Parameters of Tl2in2s3se Layered Single Crystal by Thermoluminescence
(Wiley-v C H verlag Gmbh, 2018) Gasanly, Nizami; Guler, Ipek; 101531
Thermoluminescence (TL) measurements are performed to evaluate the trap states in Tl2In2S3Se layered single crystals. TL experiments are conducted with varying temperature from 10 to 300 K and warming rates from 0.2 to 1.0 K s(-1). From the analysis of both initial rise and curve fitting methods, the activation energy of the traps is obtained as 23 meV. The Chen's method is also used to find activation energy. By means of this technique, the activation energy of the TL glow curve is calculated as 25 meV. From both Chen's method and curve fitting method, the existence of mixed order of kinetics in Tl2In2S3Se crystal is found. The cross section to capture of the trap center is found out from the results of curve fitting method. The trap distribution of the crystals is investigated with different temperatures of illumination at a constant warming rate of 0.8 K s(-1). The temperatures of illumination change from 10 to 22 K. As a result of the increase in temperatures of illumination, the peak maximum values move to higher temperatures and intensity of the TL curves decreases. This behavior shows us that quasicontinuous traps distribution is present in Tl2In2S3Se layered single crystals.
Citation - WoS: 8
Citation - Scopus: 8
Thermoluminescence in Gallium Sesquisulfide Single Crystals: Usual and Unusual Heating Rate Dependencies
(Elsevier Gmbh, 2018) Isik, M.; Gasanova, L.; Mahammadov, A.; Gasanly, N.; Guler, I; 101531
Thermoluminescence (TL) experiments were conducted for Ga2S3 crystals to obtain information about trapping parameters. TL measurements were performed from 10 to 300 K with varying heating rates in the range of 0.2-0.8 K/s. Two TL glow peaks centered at 44K (peak A) and 91 K (peak B) were observed at heating rate of beta=0.5 K/s. For peak A, TL intensity decreased whereas that for peak B increased with elevating the heating rates that means anomalous heating rate occurred for peak B. TL glow curves were analyzed using initial rise method to find activation energies of traps. Distribution of trap centers was investigated using T-max - T-stop method. Quasi-continuous distributions with increasing activation energies from 40 to 135 meV and 193 to 460 meV were attributed to trap centers A and B, respectively. (C) 2018 Elsevier GmbH. All rights reserved.