Esen, ZiyaDoğu, Merve NurBilgin, Güney MertTan, EvrenBerkay Gümüş, BerkayDericioğlu, Arcan F.2024-03-122024-03-122019Esen, Ziya...et al. "Designing thermochemical processes for ti-alloys produced by additive manufacturing techniques", 4th INTERNATIONAL CONGRESS ON 3D PRINTING (ADDITIVE MANUFACTURING) TECHNOLOGIES AND DIGITAL INDUSTRY, pp. 1383-1387, 2019.http://hdl.handle.net/20.500.12416/7559Ti-6Al-4V alloys are extensively used in biomedical, aerospace and petro-chemical applications mainly due to their high specific strength, excellent corrosion resistance and high fatigue strength. In contrast to conventional techniques, additive manufacturing techniques make possible production of parts with complex geometries in one step by minimizing the usage of raw materials. However, post heat treatment processes need to be applied to reduce residual stresses created and to get uniform controllable microstructure so as to obtain desired mechanical properties. Conventional annealing heat treatments are effective in eliminating the residual stress and increasing the ductility. But, they usually degrade the strength and result in coarsening the microstructure. In this study, thermochemical process, called thermo-hydrogen process (THP), was applied to Ti-6Al-4V alloy parts produced by selective laser melting (SLM) and electron beam melting (EBM) with the aim of increasing ductility without degrading the alloy strength. Additively manufactured parts initially hydrogenated at 650oC for 1 h under H2+Ar gas mixture and then, dehyrogenated at 700oC for 18 h under high vacuum. As a result of alloying with hydrogen and dealloying turned martensitic microstructure in SLM parts into fine + lamellar phase mixture. On the other hand, microstructural refinement in EBM parts were limited since as-manufactured parts were already composed of fine lamellar microstructure. THP prevented grain growth and grain boundary α-phase formation in SLM parts. Ductility of the alloys increased by 110 %, while the strength decreased slightly only by 10 %. However, the effect of the THP on mechanical properties of EBM samples couldn’t be observed due to their high surface roughness which induced notch effect.eninfo:eu-repo/semantics/closedAccessTi6Al4V AlloyAdditive ManufacturingThermo-Hydrogen TreatmentMechanical PropertiesConference Object13831387