The present study investigates the effect of brazing parameters on reaction layer formation, and mechanical properties of C/SiC composite-Ti6Al4V alloy joints produced by brazing technique. The wetting mechanism of the C/SiC composite surface by the Ag-CuTi-based active brazing filler alloy has also been studied and correlated with the reaction layer formation. The strength of C/SiC composite/Ti6Al4V alloy joints increased at first and then decreased with increasing reaction layer thickness. The joints with 1-mu m-thick reaction layer, which were obtained by brazing at 915 degrees C for 15 min, had the highest shear strength of 33 MPa. Brazing filler alloy presented a minimum contact angle of 15 degrees on the C/SiC composite surface at 915 degrees C during the wetting experiments. 915 degrees C and 15 min were determined to be the optimised brazing parameters to ensure almost complete wetting and a uniform reaction layer for effective adhesion of the C/SiC composite surface.